Third time lucky

At the end of last year my research group had articles published by the Royal Society’s journal  Open Science in two successive months [see ‘Press Release!‘ on November 15th, 2017 and ‘Slow moving nanoparticles‘ on December 13th, 2017].  I was excited about both publications because I had only had one article published before by the Royal Society and because the Royal Society issues a press release whenever it publishes a new piece of science.  However, neither press release generated any interest from anyone; probably because science does not sell newspapers (or attract viewers) unless it is bad news or potentially life-changing.  And our work on residual stress around manufactured holes in aircraft or on the motion of nanoparticles does not match either of these criteria.

Last month, we did it again with an article on ‘An experimental study on the manufacture and characterization of in-plane fibre-waviness defects in composites‘.  Third time lucky, because this time our University press office were interested enough to write a piece for the news page of the University website, entitled ‘Engineers develop new method to recreate fibre waviness defects in lab‘.  Fibre waviness is an issue in the manufacture of structural components of aircraft using carbon fibre reinforced composites because kinks or waves in the fibres can cause structural weaknesses.  As part of his PhD, supported by Airbus and the UK Engineering and Physical Sciences Research Council (EPSRC), Will Christian developed an innovative technique to generate defects in our lab so that we can gain a better understanding of them. Read the article or the press release to find out more!

Image shows fracture through a waviness-defect in the top-ply of a carbon-fibre laminate observed in a microscope following sectioning after failure.

Reference:

Christian WJR, DiazDelaO FA, Atherton K & Patterson EA, An experimental study on the manufacture and characterisation of in-plane fibre-waviness defects in composites, R. Soc. open sci. 5:180082, 2018.